Backing of
Wear Liner in all makes & Model of Cone and Gyratory Crusher |
| |
|
100% Solids Epoxy Compound |
 |
| High compressive &
impact strength |
| Excellent
volumetric stability – no formation of gap between backing and
liners or main frame |
|
Salient
Feature |
Typical Properties |
|
Safe more economical than molten zinc |
|
: 21000 |
|
Tensile Strength, PSI |
: 5000 |
|
Hardness , Shore D |
: 87 |
|
Simple in application – just mix Resin &
Hardener and pour in to a cavity |
Maximum Operating
Temperature oC |
: 105 |
|
Mixing Ratio By
Weight (R:H) |
: 23.66 (R) + 1 (H) |
|
Pot Life at 30o
C, minutes |
: 30 |
|
Full cure at 30o
C hours |
: 6 |
|
Minimal
amount of filler settlement |
Colour
|
Red |
|
Specific gravity |
: 1.42 |
| Mixed Viscosity , CPS |
: 10000 |
|
Application Instruction : |
Surface Preparation: |
| All Metallic parts should
be free of rust , dirt , grease , oil etc., Seal all voids and
gaps to prevent leakage. Coat bowl liner , threaded portions
release agent for easy removal |
| |
|
Mixing: |
| Stir
Resin box individually for atleast 3 minutes using slow speed
stirrer to disperse any settlement that may have taken place
during storage. Add entire contents of Hardener slowly but
continuously to Resin while simultaneously stirring the resin.
Mix both the components together for approximately 5 minutes.
Move stirrer up , down and around the sides of container till
achievement of uniforms colours. Care should be taken to avoid
excess air entrapment and to ensure that no Resin and Hardener
remains unmixed prior to pouring, as this can lead to soft
pockets. |
| |
|
Application: |
| Pour
mixture from one place to fill the cavity to avoid air gaps. Use
tin sheet or cardboard to direct the flow if required. Repeat
the procedure for succeeiding Kits. During cold condition
pre-heat the substrate until warm to touch or indirect heat may
be applied for shortening the cure time of epoxies.. |
| |
|
General Instructions: |
o In high ambient
temperatures and for larger volumes compound will cure faster
,apply in thin layers
o In low temperatures and for small volumes
compound takes longer to cure , use indirect heat if require
|
o The compound after mixing are to be used
within specified pot life. The material stiffened after pot
life should
discarded.
o Tools and equipment should be cleaned
before skin formation.
o Refer “Chemical Resistant Chart” for
chemical compatiability or contact us for on site technical
support service.
|
|
Warning:- In case of eye contact or skin irritation immediately
flush with plenty of water and sought
medical attention |
| |
| Note |
|
The information contained herein , is to
the best of our knowledge & accurate. However since conditions
of handling and Usage are beyond our control , we accept no
liability either directly or indirectly. The conduct of test
application is always Recommended . Due to continual upgradation
of products above date is subject to changes without notice.
This supersedes our previously issued Technical Data Sheets |
|
|